Inhibition of the Corrosion of Zinc in H2SO4 by 9-deoxy-9a-aza-9a-methyl-9a-homoerythromycin A (Azithromycin)

 

S.A. Odoemelam,1 E.C. Ogoko,1 B.I. Ita,2 N.O. Eddy3,*

 

1Department of Chemistry, Michael Okpara University of Agriculture, Umudike, Abia State, Nigeria

2Department of Chemistry, University of Calabar, Calabar, Nigeria

3Department of Chemistry, Ahmadu Bello University, Zaria, Kaduna State, Nigeria

 

Received 24 September 2008; accepted 6 November 2008

 

Abstract

Inhibition of the corrosion of zinc in various concentrations (0.01 to 0.05 M) of H2SO4 was studied using weight loss and hydrogen evolution methods of monitoring corrosion. The results revealed that various concentrations of azithromycin (0.0001 to 0.0005 M) inhibited the corrosion of zinc in H2SO4 at different temperatures (303 to 333 K). The concentration of H2SO4 did not exert significant impact on the inhibition efficiency of azithromycin, but inhibition efficiencies were found to decrease with increase in the concentration of the inhibitor. Values of inhibition efficiency obtained from the weight loss measurements correlated strongly with those obtained from the hydrogen evolution measurements. The activation energies for the corrosion of zinc inhibited by azithromycin were higher than the values obtained for the blank. Thermodynamic data revealed that the adsorption of azithromycin on the surface of zinc was endothermic (values of enthalpies of adsorption were positive), spontaneous (values of free energies of adsorption were negative) and was consistent with the adsorption model of Langmuir.

Keywords: Corrosion inhibition, zinc, azithromycin.

 

 

Full text only in PDF format

Texto disponível em PDF

 

 

References

1. Y.K. Agrawal, J.D. Talati, M.D. Shah, M.N. Desai and N.K. Shah, Corrosion Sci. 46 (2004) 633.          [ Links ]

2. S.A. Odoemelam and N.O. Eddy, Mat. Sci. 4(1) (2008) 1.        [ Links ]

3. B.I. Ita, J. Nig. Envr. Soc. 1(1) (2004) 113.

4. S. Acharya and S.N. Upadhyay, Indian Inst. Met.67 (3) 297.

5. H. Wang, X. Wang, H. Wang, L. Wang and A. Liu, J. Mol. Model. 13 (2007) 147.        [ Links ]

6. B. Gomez, N.V. Likhanova, M.A. Dominguez-Aguilar, R. Martinez-Palou, A. Vela and J. Garzquez, J. Phys. Chem. 110 (2006) 8928.        [ Links ]

7. S.L. Li, Y.G. Wang, S.H. Chen, R. Yu, S.B. Lei, H.Y. Ma and D.X. Liu, Corrosion Sci. 41 (1999) 1749.        [ Links ]

8. E.S. El Ashry, A. El Nemir, S.A. Essawy and S. Ragah, ARKIVOC xi (2006) 205.

9. J. Fang and J. Lie, J. Mol Struct. 593 (2002) 179.        [ Links ]

10. E.S. El Ashry, A. El Nemir, S.A. Essawy and S. Ragah, Electrochimica Acta 51 (2006) 1957.        [ Links ]

11. R. Solmaz, G. Kardas, B. Yaziei and M. Erbil, Protect. of Metals 41(6) (2005) 581.        [ Links ]

12. K.S. Rajappa and T.V. Venkatesha, Turk. J. Chem. 27 (2002) 189.

13. E.E. Oguzie,  Pigment and Resin Technol. 34(6)  (2005) 321.        [ Links ]

14. J. Arauyo, R. Ortiz, W. Velasquez and J.M. Ortega, Portugaliae Electrochimica Acta 24 (2006) 71.        [ Links ]

15. N.O. Eddy and A.S. Ekop, Mat. Sci. 4(1) (2008) 10.        [ Links ]

16. P. Atkins, Physical Chemistry, 7th edition. Oxford: Oxford press. (2002).

17. K.K. Sharma and L.K. Sharma, A textbook of physical chemistry. 4th revised edition. India: Vikas Pub. House. PVT Ltd. (2004).

18. N.O. Eddy, Inhibition of the corrosion of mild steel in H2SO4 by some antibiotics, Ph.D. Thesis, University of Calabar. 2008.

19. N.O. Eddy and E.E. Ebenso, Afri. J. Pure & Appl. Chem. 2(6) 1.

20. N.O. Eddy, A.O. Odiongenyi and S.A. Odoemelam, Adv. in Nat. & Appl. Sci. 2(1) (2008) 35.        [ Links ]

 

* Corresponding author. E-mail address: nabukeddy@yahoo.com

Creative Commons License All the contents of this journal, except where otherwise noted, is licensed under a Creative Commons Attribution License