Inhibition of metallic corrosion using ficus extract

A.Y. El-Etre,* Z. El-Tantawy

Chemistry Department, Faculty of Science, Benha University, Benha, Egypt

 

 

Abstract

The inhibitive action of the extract of Ficus nitida leaves toward general and pitting corrosion of C-steel, nickel and zinc in different aqueous media was investigated. Weight loss measurements, potentiostatic and potentiodynamic polarization techniques were used in this study. It was found that the presence of ficus extract in the corrosive media (acidic, neutral or alkaline) decreases the corrosion rates of the three tested metals. The inhibition efficiency increases as the extract concentration is increased. The inhibition efficiency depends on the type of corroded metal and on the corrosive solution. It was also found that the presence of ficus extract in the chloride containing solution shifts the pitting potentials of the tested metals toward the noble direction. The inhibitive action of ficus extract is discussed in view of adsorption of its components, the poly aromatic compounds, friedelin, epifriedelanol and nitidol, on the metal surface. It was found that such adsorption follows Langmuir adsorption isotherm. The calculated values of the free energy of adsorption indicated that the adsorption process is spontaneous.

Keywords: C-steel, nickel, zinc, corrosion inhibition, natural products, ficus.

 

Texto disponível em PDF

Full text only in PDF format

 

References

1. Ling-Guang Qiu, An-Jian Xie and Yu-Hua Shen, Corros. Sci. 47 (2005) 273.        [ Links ]

2.  K. Sapre, S. Seal, P. Jepson, H.B. Wang, Z. Rahman and T. Smith, Corros. Sci. 45 (2003) 59.

3.  F. Zucchi, G. Trabanelli, C. Monticelli and V. Grassi, Corros. Sci. 42 (2000) 505.

4.  Rong Guo, Tianqing Liu and Xun Wei, Colloids Surf. 209 (2002) 37.

5.  M.R. Laamari, A. Derja, J. Benzakour and M. Berraho, J. Electroanal. Chem. 569 (2004) 1.

6. E.E. Foad El-Sherbini, S.M. Abdel Wahaab and M. Deyab, Mater. Chem. Phys. 89 (2005) 183.

7.  M.A. Pech-Canul and P. Bartolo-Pérez, Surf. Coat. Tech. 184 (2004) 133.

8. M. Abdallah, Corros. Sci. 45 (2003) 2705.

9. A.Y. El-Etre, M. Abdallah and Z.E. El-Tantawy, Corros. Sci. 47 (2005) 385.

10. A.Y. El-Etre and M. Abdallah, Corros. Sci. 42 (2000) 731.

11. A.Y. El-Etre, Corros. Sci. 45 (2003) 2485.

12. A.Y. El-Etre, Corros. Sci. 40 (1998) 1845.

13. R.M. Saleh, A.A. Ismail and A.A. El-Hosary, Br. Corros. J. 17 (1982) 131.

14. S.A. Verma and G.N. Mehta, Bull. Electrochem. 15 (1999) 67.

15. S. Martinez and I. Stagljar, J. Molecular Structure 640 (2003) 167.

16. M.A. Quraishi, I.H. Farooqi and P.A. Saini, Corrosion 55 (1999) 493.

17. I.O’M. Bockris and D.A. Swinkls, J. Electrochem. Soc. 111 (1964) 736.

18. M.H.A. Elgamal, B.A.H. El-Tawil and M.B.E. Fayez, Naturwissenschaften 62 (1975) 486.

19. M. Behari, K.U. Rani, T. Matsumoto and N. Shimizu, Curr. Agric. 8 (1984) 73.

 

*Corresponding author. E-mail address: aliyousry@hotmail.com