vol.36 número6Comparative Corrosion Resistance of Molybdate Conversion Coatings Containing SiO2 or TiO2 NanoparticlesEvaluation of the Electrochemical Impedance Measurement of Mild Steel Corrosion in an Acidic Medium, in the Presence of Quaternary Ammonium Bromides índice de autoresíndice de assuntosPesquisa de artigos
Home Pagelista alfabética de periódicos  

Serviços Personalizados

Journal

Artigo

Indicadores

Links relacionados

  • Não possue artigos similaresSimilares em SciELO

Compartilhar


Portugaliae Electrochimica Acta

versão impressa ISSN 0872-1904

Resumo

EL IBRAHIMI, Brahim et al. Cysteine Duality Effect on the Corrosion Inhibition and Acceleration of 3003 Aluminium Alloy in a 2% NaCl Solution. Port. Electrochim. Acta [online]. 2018, vol.36, n.6, pp.403-422. ISSN 0872-1904.  https://doi.org/10.4152/pea.201806403.

Cysteine's action on 3003 aluminum alloy dissolution in a 2% NaCl solution, at different pH values, has been investigated. Weight-loss measurements, potentiodynamic polarization and electrochemical impedance at OCP were performed. The surface morphology was analyzed by SEM. The main results showed that the alloy underwent severe corrosion at 2 and 11 pH values, as compared to at 5 and 8 pH values. Furthermore, a duality effect of cysteine was noted, as it acted as a corrosion inhibitor or accelerator, depending on its concentration, and on the solution's pH value. This particular behavior can be related to the instability of the formed film adsorbed onto the metal surface. All these findings show the high complexity of cysteine action on 3003 aluminum alloy, under the investigated conditions.

Palavras-chave : cysteine; AA3003; corrosion; pH; 2% NaCl.